99.99% Lanthanum ocsid CAS 1312-81-8
Manyleb
Lanthanum ocsid | 3N | 4N | 4.5N |
TREO% | ≥98 | ≥99 | ≥99 |
La purdeb ac amhureddau cymharol prin y ddaear | |||
La2O3/TREO % | ≥99.9 | ≥99.99 | ≥99.995 |
CeO2/TREO % | ≤0.05 | ≤0.007 | ≤0.004 |
P6O11/TREO % | ≤0.01 | ≤0.001 | ≤0.0005 |
Nd2O3/TREO % | ≤0.01 | ≤0.001 | ≤0.0005 |
Sm2O3/TREO % | ≤0.01 | ≤0.001 | ≤0.0005 |
Y2O3/TREO % | ≤0.01 | ≤0.001 | ≤0.0005 |
Amhuredd daear nad yw'n brin | |||
Fe2O3 % | ≤0.01 | ≤0.005 | ≤0.005 |
SiO2 % | ≤0.02 | ≤0.015 | ≤0.01 |
CaO % | ≤0.08 | ≤0.05 | ≤0.03 |
Na % | ≤0.02 | ≤0.01 | ≤0.01 |
MnO2 % | ≤0.01 | ≤0.005 | ≤0.005 |
AL2O3 % | ≤0.01 | ≤0.007 | ≤0.005 |
PbO % | ≤0.01 | ≤0.005 | ≤0.003 |
Cl-% | ≤0.08 | ≤0.06 | ≤0.05 |
Ymbelydrol | 1Bq/g | ||
LOI (1000 ℃ 2 awr) | ≤ 3.0 | ≤ 2.0 | ≤2.0 |
Cais
Defnyddir lanthanum ocsid yn bennaf wrth gynhyrchu gwydr optegol manwl a ffibrau optegol.Defnyddir hefyd yn y diwydiant electroneg fel cynwysorau ceramig, asiant dopio cerameg piezoelectrig.Fe'i defnyddir hefyd fel deunydd crai ar gyfer paratoi lanthanum boride, ac fel catalydd ar gyfer gwahanu a phuro petrolewm.
Pacio a Storio
1kg/25kg neu fel cais;
Amodau storio: tymheredd ystafell, sych, wedi'i selio.